Alloy 400
Nickel Based Alloy for Oil & Gas
HIGH STRENGTH
Certified Standards: |
ASTM B164 |
ASME SB164 |
ASTM B564 |
ASME SB564 |
ASME Sec.II Part B/SB 164/564 |
SAE-AMS 4675 (Chemistry only) |
BS 3076-89 NA13 |
UNS N04400 |
Nace MR01-75 / ISO15156 |
Nace MR01-03 |
PED 97/23/EC |
Minimum mechanical properties to ASTM A370 |
Rp0.2% (yield) |
275Mpa / 40KSI |
Rm (ultimate tensile) |
551MPa / 80KSI |
Elongation (A4) |
30% |
Reduction of Area |
Information only |
Hardness (HRc) |
35 Max |
Hardness (HRb) |
Information only |
Typical mechanical properties to ASTM A370 |
Rp0.2% (yield) |
380 to 414Mpa / 55 to 60KSI |
Rm (ultimate tensile) |
586 to 620MPa / 85 to 90KSI |
Elongation (A4) |
35 to 40% |
Reduction of Area |
60 to 70% |
Hardness (HRc) |
<20 |
Hardness (HRb) |
85 / 90 |
Alloy 400 Round Bar Size Range ex-stock |
Machined Round Bar - sawn to length if required |
Dia. Metric (mm) |
Dia. Imp. (inch) |
Tol. |
15.88 |
0.625 |
Peeled K11 |
19.05 |
0.750 |
Peeled K11 |
22.23 |
0.875 |
Peeled K11 |
25.40 |
1.000 |
Peeled K11 |
28.58 |
1.125 |
Peeled K11 |
31.75 |
1.250 |
Peeled K11 |
34.93 |
1.375 |
Peeled K11 |
38.10 |
1.500 |
Peeled K11 |
44.45 |
1.750 |
Peeled K11 |
50.80 |
2.000 |
Peeled K11 |
57.15 |
2.250 |
Peeled K11 |
63.50 |
2.500 |
Peeled K11 |
69.85 |
2.750 |
Peeled K11 |
76.20 |
3.000 |
Peeled K11 |
82.55 |
3.250 |
Peeled K11 |
88.90 |
3.500 |
Peeled K11 |
95.25 |
3.750 |
Peeled K11 |
101.60 |
4.000 |
Peeled K11 |
107.95 |
4.250 |
Peeled -0/+1mm |
114.30 |
4.500 |
Peeled K11 |
120.65 |
4.750 |
Peeled -0/+1mm |
127.00 |
5.000 |
Peeled K11 |
139.70 |
5.500 |
Peeled K11 |
152.40 |
6.000 |
Peeled -0/+1mm |
165.10 |
6.500 |
Peeled -0/+1mm |
177.80 |
7.000 |
Peeled -0/+1mm |
190.50 |
7.500 |
Peeled -0/+1mm |
203.20 |
8.000 |
Peeled -0/+1mm |
View ISO Tolerances